ALKON CAST 204

캘더리스

BAG(=25KG)
PALLET(=1000KG)
PRODUCT TYPE : Alumina - Silica product (Medium cement castable) 
Maximum recommended temperature : 1200
Main component : Bauxite
Type of bond : Hydraulic
Appearence : Dry
Packaging : Sacks
Shelf life : 6months in temperate conditions
Installation method : Vibrating
Maximum grain size : 5 mm
Material required : 2.82 T/m3
Drinking water required for mixing on site : 4.5 / 6.0 liters per 100kg of dry material : to be adjusted for desired consistency

     

    -알미늄 접촉부위에서의 내식성 탁월 (Non-wetting 성분함유)
    -Calde cast 1600 대체 및 보수용으로도 사용가능 (기존 모재와 부착성이 매우 우수)
    -시공 용이하며 강도 높음 (>1400kg중/cm2)
    -용해실 바닥, 러너, 래들 등 다용도 사용가능

         

            제품 속성 평균값 단위

            화학 분석

            Al2O3

            SiO2

            CaO

            Fe2O3

             

            79.5

            14.0

            4.3

            1.1

             

            %

            %

            %

            %

            물리적 속성

            Bulk density

            after drying at 110 

            after firing at 800 

            Cold crushing strength

            after drying at 110 ℃

            after firing at 800 ℃

            after firing at 1200 ℃

            Permanant linear change

            after firing at 800 ℃

            after firing at 1200 ℃

            Thermal conductivity

            at a mean temperature of 800 ℃

            at a mean temperature of 1000 ℃

            at a mean temperature of 1200 ℃

             

             

             

            2.86

            2.80

             

            150

            140

            120

             

            -0.2

            +0.0

             

            2.66

            2.52

            2.44

             

             

             g/cm3 

            g/cm3

             

            MPa

            MPa

            MPa

             

            %

            %

             

            W/mK

            W/mK

            W/mK